| 簡稱 | 英文 | 中文 | ||
| ABS | Acrylonitrile-Butadiene-Styrene | 丙烯腈-丁二烯-苯乙烯共聚合物 | ||
| ASA | Acrylic-styrene-acrylonitrile | 丙烯酸-苯乙烯-丙烯腈 | ||
| CA | Cellulose Acetate | 纖維素醋酸酯 | ||
| CAP | Cellulose Acetate Propionate | 纖維素醋酸丙酸酯 | ||
| CB | Cellulose Butyrate | 纖維素酪酸酯 | ||
| CP | Cellulose Propionate | 纖維素丙酸酯 | ||
| CTFE | Polychlorotrifluoroethylene | 聚一氯三氟乙烯 | ||
| EAA | Ethylene Acrylic Acid(TP) | 乙烯丙烯酸 | ||
| EAE | Ethylene Acrylic Ester(TP) | 乙烯丙烯酸乙酯 | ||
| ECTFE | Ethylene-chlorotrifluoroeethylene | 乙烯一氯三氟乙烯共聚合物 | ||
| EMA | Ethylene Methyl Acrylate(TP) | 乙烯甲基丙烯酸酯 | ||
| EMAA | Ethylene Methacrylic Acid | 乙烯丙烯酸甲酯 | ||
| ENBA | Ethylene N-Butyl Acrylate(TP) | 乙烯丁基丙烯酸酯 | ||
| ETFE | Copolymer of ethylene and chlorotetrafluoroethylene | 乙烯一氯四氟乙烯共聚合物 | ||
| EVA | Ethylene Vinyl Acetate(TP) | 乙烯乙基丙烯酸酯 | ||
| EVOH | Ethylene Vinyl Silane(TP) | 乙烯乙基醇 | ||
| FEP | Fluorinated ethylene-propylene | 氟化乙烯丙烯 | ||
| HDPE | High density Polyethylene | 高密度聚乙烯 | ||
| LCP | Liquid crystal polyester | 液晶聚酯 | ||
| LDPE | Low density Polyethylene | 低密度聚乙烯 | ||
| LLDPE | Linear Low density Polyethylene | 線性低密度聚乙烯 | ||
| IONOMER | lonomer | 離子聚合物 | ||
| MDPE | Medium density Polyethylene | 中密度聚乙烯 | ||
| PA | Polyamide | 聚醯胺 | ||
| PA11 | Polyamide 11 | 聚醯胺 11 | ||
| PA12 | Polyamide 12 | 聚醯胺 12 | ||
| PA4/6 | Polyamide 4/6 | 聚醯胺4/6 | ||
| PA6 | Polyamide 6 | 聚醯胺 6 | ||
| PA6/10 | Polyamide 6/10 | 聚醯胺 6/10 | ||
| PA6/12 | Polyamide 6/12 | 聚醯胺 6/12 | ||
| PA6/6 | Polyamide 6/6 | 聚醯胺 6/6 | ||
| PA6/9 | Polyamide 6/9 | 聚醯胺 6/9 | ||
| PAI | Polyamide-imide | 聚醯胺醯亞胺 | ||
| PBT | Polybutylene terephathalate | 聚對苯二甲酸二丁酯 | ||
| PC | Polycarbonate | 聚碳酸酯 | ||
| PCT | Polycarbonate hexandimethanol Terephthalate | 聚環已醇二乙酯 | ||
| PEC | Polyethylene-Chlorinated | 氯化聚乙烯 | ||
| PEEK | Polyetheretherketone | 聚醚醚酮 | ||
| PEI | Polyetherimide | 聚醚醯亞胺 | ||
| PES | Polyethersulfone | 聚醚碸 | ||
| PET | Polyethylene terephathalate | 聚對苯二甲酸二乙酯 | ||
| PETG | Glycol-Polyethylene terephathalate | 二元醇改質聚對苯二甲酸二乙酯 | ||
| PFA | Perfluoroalkoxy | 過氟烷氧基 | ||
| PI | Polyimide | 聚醯亞胺 | ||
| PK | Polyketone | 聚酮 | ||
| PMMA | Polymethylmethacrylic | 聚甲基丙烯酸甲酯 | ||
| PMP | Polymethylpentene | 聚甲基戊烯 | ||
| Polyolefin | -------------- | 聚烯烴 | ||
| POM | Polyacetal | 聚縮醛 | ||
| PP | Polypropylene(TP) | 聚丙烯 | ||
| PPA | Polyphthalamide | 聚酞酸酯 | ||
| PPE | Polyphenylene Ether | 聚苯醚 | ||
| PPO | Polyphenylene Oxide | 聚氧化二甲苯 | ||
| PPS | Polyphenylene Sulfide | 聚硫化苯 | ||
| PS | Polystyrene(TP) | 聚苯乙烯 | ||
| PSF | Polysulfone(TP) | 聚碸 | ||
| PTFE | Polytetrafluorothylene | 聚四氟乙烯 | ||
| PU | Polyurethane(TP) | 聚氨基甲酸乙酯 | ||
| PVC | Polyvinyl Chloride(TP) | 聚氯乙烯 | ||
| PVDC | Polyvinyl Dichloride | 聚二氯乙烯 | ||
| PVDF | Polyvin ylidene fluoride | 聚氟化乙二烯 | ||
| SAN(AS) | Styrene-Acrylonitrile | 苯乙烯-丙烯腈 | ||
| SB | Styrene-Butadiene | 苯乙烯-丁二烯 | ||
| SMA | Styrene Maleic Anhydride | 苯乙烯-馬來酐 | ||
| TPE | Thermoplastic Elastomer (TPE) | 熱塑性彈性體 | ||
| TPO | Thermoplastic Polyolefin(TPO) | 熱塑性聚烯烴 | ||
| 改善TPE与尼龙PA之粘接性的方法 | ||||
| TPE包胶尼龙（主要指PA6,PA66及其加纤改性工程塑料）,主要应用于厨具餐具手柄,电动电钻工具手柄,电器产品配件等等.TPE软胶可通过配方改性来调整硬度,用于包胶尼龙的TPE软胶,一般硬度范围在ShoreA40~80度,其中以硬度60度左右最为常见.TPE与尼龙PA的复合注塑|包覆成型,一般采用双色注塑机或者普通注塑机（需开两套模具，一套模具注塑尼龙制件,另一套模具用于将TPE软胶包覆成型到PA尼龙表面,先注塑尼龙制件,再将TPE注塑粘射到尼龙件表面）等设备来完成.目前,很多用户在做TPE包胶尼龙的产品时，常遇到TPE与尼龙粘接性不好的问题，笔者现做如下浅析，供读者参考： TPE包胶尼龙PA的粘接性分析—— 目前在国内TPE弹性体改性行业，不同的TPE弹性体厂家的TPE粘接尼龙PA料的技术成熟度不同。从材料的属性分析，TPE与尼龙PA的粘接本身有一定的难度，因为两种材料微观分子极性差距较大，自身相容性比较差，需通过引入接枝性材料可改善TPE与尼龙的接着性，这是指从材料配方角度而言。再就是从材料加工而言，必须使得TPE与尼龙材料具有相接近的加工温度，如PA尼龙的注塑加工温度在250~260度，那么，二次注塑TPE的时候，TPE的成型加工温度就要接近这个温度，要达到240~250度左右，接近但略低于尼龙注塑温度. TPE与PA尼龙粘接性不好的改善办法—— 1.从配方角度着手，可改善TPE与PA相容性，从而提升二者的粘接性； 2.适当提高TPE注塑加工温度.粘尼龙PA的TPE都具有较高的塑化温度，因此必须要有足够的TPE加工温度，达到TPE与尼龙PA良好粘接所必须的温度条件. 3.尼龙制件在二次注塑前的预热处理.实际在TPE材料包胶尼龙加工工艺中，可以先将PA尼龙制件用烤箱加热，再趁热放入包胶模具，将TPE材料立即注塑上去，可改善TPE与尼龙的粘接性能. 4.从产品设计入手.可在尼龙制件上无关紧要的位置打孔，在软胶包覆位置边缘设置锯齿槽，通过嵌入注塑或增大TPE与PA的接触面，可改善二者的粘接性. | ||||