P M C – T 376J

PMC-T376J Black Phenolic is a two-stage, heat resistant/electrical molding material offering excellent mold process-ability and optimized Cure cycles. Typical applications include circuit breaker, electrical terminal strips, telecommunication application, etc.

Typical Physical Properties Method Metric

Grade ASTM

JIS Value Unit

Specific Gravity D792 K7112 1.56 --- Water Absorption D570 K6911 0.16 % General

Molding Shrinkage D955 K6915 0.0095 m/m Charpy Impact D256 K7111 3.5 Kgf/cm Izod Impact D256 K6911 3.0 Kgf/cm Flexural Strength D790 K7203 95 MPa Tensile Strength D638 K6911 56 MPa Compressive Strength D695 K6911 210 MPa

Mechanical

Deflection Temp.

D8 K7207 190 0

C

Dielectric Strength D149 K6915 13 KV/mm Insulation Resistance(N) D257 K6915 10E+10 Ohm Insulation Resistance(B) D257 K6915 10E+8 Ohm Electrical

V olume Resistivity

D257

K6911

10E+12 Ohm-cm

UL 94 Flame Class 0.60 mm/V-0CTI PLC Level 4 --- D495 PLC Level

4

---

UL File

RTI 150 0

C

The typical values listed are results obtained from the testing of standard specimens

using the stated test procedures, with said specimens molded under controlled laboratory conditions from representative samples of the product

V e r 1s s t t

/2004

301 SONGKIANG ROAD,7TH FL. TAIPEI, TAIWAN TEL:(02)25038131 FAX:(02)25033378

UL File: E59481Form : Granular Storage Life : 1 Year

CCP

P M C–T385J

PMC-T385J Black Phenolic is a two-stage, general purpose molding

material offering excellent mold process-ability and optimized

Cure cycles. Typical applications include cookware handles and knobs,

Houseware appliance parts, etc.

Typical Physical Properties Method Metric

Grade ASTM JIS

Value

Unit Specific Gravity D792 K7112 1.42 ---

Water Absorption D570 K6911 0.3 %

General

Molding Shrinkage D955 K6915 0.0125 m/m

Charpy Impact D256 K7111 3.5 Kgf/cm

Izod Impact D256 K6911 3.0 Kgf/cm

Flexural Strength D790 K7203 95 MPa

Tensile Strength D638 K6911 56 MPa

Compressive Strength D695 K6911 210 MPa Mechanical

Deflection Temp. D8 K7207 160 0C

Dielectric Strength D149 K6915 10 KV/mm

Insulation Resistance(N) D257 K6915 1E+10 Ohm

Insulation Resistance(B) D257 K6915 1E+8 Ohm Electrical

V olume Resistivity D257 K6911 1E+12 Ohm-cm

UL 94 Flame Class 6.0 mm/V-0

CTI PLC Level 4 ---

D495 PLC Level 7 --- UL File

RTI 150

0C

The typical values listed are results obtained from the testing of standard specimens

using the stated test procedures, with said specimens molded under controlled

laboratory conditions from representative samples of the product

V e r1s s t t/2004

301 SONGKIANG ROAD,

7TH FL. TAIPEI, TAIWAN

TEL:(02)25038131

FAX::(02)25033378

UL File: E59481

Form : Granular

Storage Life : 1 Year

CCP

P M C – T 310

PMC-T310 Black Phenolic is a two-stage, mechanical purpose molding material offering excellent mold process-ability and optimized Cure cycles. Typical applications include automotive interior parts, circuit breaker and container covers, etc.

Typical Physical Properties Method Metric

Grade ASTM

JIS Value Unit

Specific Gravity D792 K7112 1.53 --- Water Absorption D570 K6911 0.15 % General

Molding Shrinkage D955 K6915 0.08 m/m Charpy Impact D256 K7111 4.5 Kgf/cm Izod Impact D256 K6911 3.8 Kgf/cm Flexural Strength D790 K7203 125 MPa Tensile Strength D638 K6911 56 MPa Compressive Strength D695 K6911 220 MPa

Mechanical

Deflection Temp.

D8 K7207 190 0

C

Dielectric Strength D149 K6915 14 KV/mm Insulation Resistance(N) D257 K6915 E+11 Ohm Insulation Resistance(B) D257 K6915 5E+9 Ohm Electrical

V olume Resistivity

D257

K6911

1E+13 Ohm-cm

UL 94 Flame Class 3.0 mm/V-0CTI PLC Level 4 --- D495 PLC Level

5

---

UL File

RTI 150 0

C

The typical values listed are results obtained from the testing of standard specimens

using the stated test procedures, with said specimens molded under controlled laboratory conditions from representative samples of the product

V e r 1s s t t

/2004

301 SONGKIANG ROAD,7TH FL. TAIPEI, TAIWAN TEL:(02)25038131 FAX::(02)25033378

UL File: E59481Form : Granular Storage Life : 1 Year

P M C–T355J

PMC-T355J Black Phenolic is a two-stage, mechanical purpose molding

material offering excellent mold process-ability and optimized Cure

cycles. Typical applications include automotive interior parts, circuit

breaker and drive train components, etc.

Typical Physical Properties Method Metric

Grade ASTM JIS

Value

Unit Specific Gravity D792 K7112 1.47 ---

Water Absorption D570 K6911 0.2 %

General

Molding Shrinkage D955 K6915 0.01 m/m

Charpy Impact D256 K7111 4.0 Kgf/cm

Izod Impact D256 K6911 3.5 Kgf/cm

Flexural Strength D790 K7203 115 MPa

Tensile Strength D638 K6911 65 MPa

Compressive Strength D695 K6911 210 MPa Mechanical

Deflection Temp. D8 K7207 180 0C

Dielectric Strength D149 K6915 13 KV/mm

Insulation Resistance(N) D257 K6915 E+11 Ohm

Insulation Resistance(B) D257 K6915 E+9 Ohm Electrical

V olume Resistivity D257 K6911 1E+13 Ohm-cm

UL 94 Flame Class 0.62 mm/V-0

CTI PLC Level 3 ---

D495 PLC Level 5 --- UL File

RTI 150

0C

The typical values listed are results obtained from the testing of standard specimens

using the stated test procedures, with said specimens molded under controlled

laboratory conditions from representative samples of the product

V e r1s s t t/2006

UL File: E59481

Form : Granular

Storage Life : 1 Year下载本文