Physical Properties
| 物理性质 | Metric 公 | English 英语 | Comments 评论 | |
| Specific Gravity 比重 | 1.20 g/cc 1.20克/立方厘米 | 1.20 g/cc 1.20克/立方厘米 | ASTM D 792 ASTM D 792 | |
| Density 密度 | 1.19 g/cc 1.19克/立方厘米 | 0.0430 lb/in³ 0.0430磅/³ | ASTM D 792 ASTM D 792 | |
| Water Absorption 吸水率 | 0.150 % 0.150％ @Time 800 sec @时间800秒 | 0.150 % 0.150％ @Time 24.0 hour @时间24.0小时 | ASTM D 570 ASTM D 570 | |
| Moisture Absorption at Equilibrium 平衡吸湿量 | 0.350 % 0.350％ @Temperature 23.0 °C @温度23.0°C | 0.350 % 0.350％ @Temperature 73.4 °F @温度73.4°F | ASTM D 570 ASTM D 570 | |
| 0.580 % 0.580％ @Temperature 100 °C @温度100°C | 0.580 % 0.580％ @Temperature 212 °F @温度212°F | ASTM D 570 ASTM D 570 | ||
| Linear Mold Shrinkage, Flow 线性成型收缩率，流动 | 0.00500 - 0.00700 cm/cm 0.00500 - 0.00700厘米/厘米 @Thickness 3.20 mm @厚度3.20毫米 | 0.00500 - 0.00700 in/in 0.00500 - 0.00700 / @Thickness 0.126 in @厚度0.126 | SABIC Method SABIC方法 | |
| Melt Flow 熔体流动 | 10.5 g/10 min 10.5 g/10分钟 @Load 1.20 kg, 在某负载时1.20公斤， Temperature 300 °C 温度300°C | 10.5 g/10 min 10.5 g/10分钟 @Load 2.65 lb, 在某负载时2.65磅， Temperature 572 °F 温度572°F。 | ASTM D 1238 ASTM D 1238 | |
| Mechanical Properties 力学性能 | Metric 公 | English 英语 | Comments 评论 | |
| Hardness, Rockwell M 硬度计，洛氏M | 70.0 70.0 | 70.0 70.0 | ASTM D 785 ASTM D 785 | |
| Hardness, Rockwell R 硬度计，洛氏ŕ | 118 118 | 118 118 | ASTM D 785 ASTM D 785 | |
| Tensile Strength at Break 拉伸断裂强度 | 68.0 MPa 68.0兆帕 | 9860 psi 9860 PSI | Type I, 50 mm/min; ASTM D 63850毫米/分钟，ASTM D-638 | |
| Tensile Strength, Yield 抗拉强度，屈服 | 62.0 MPa 62.0兆帕 | 90 psi 90 PSI | Type I, 50 mm/min; ASTM D 63850毫米/分钟，ASTM D-638 | |
| Elongation at Break 断裂伸长率 | 130 % 130％ | 130 % 130％ | Type I, 50 mm/min; ASTM D 63850毫米/分钟，ASTM D-638 | |
| Elongation at Yield 屈服伸长率 | 7.00 % 7.00％ | 7.00 % 7.00％ | Type I, 50 mm/min; ASTM D 63850毫米/分钟，ASTM D-638 | |
| Flexural Modulus 弯曲模量 | 2.34 GPa 2.34 GPA | 339 ksi 339 KSI | 1.3 mm/min, 50 mm span; ASTM D 790 1.3毫米/分钟，跨度50毫米; ASTM D 790 | |
| Flexural Yield Strength 弯曲屈服强度 | 96.0 MPa 96.0兆帕 | 13900 psi 13900 PSI | 1.3 mm/min, 50 mm span; ASTM D 790 1.3毫米/分钟，跨度50毫米; ASTM D 790 | |
| Izod Impact, Unnotched 梁缺口冲击强度，无缺口 | 32.04 J/cm 32.04 J /厘米 @Temperature 23.0 °C @温度23.0°C | 60.02 ft-lb/in 60.02 ft-lb/in @Temperature 73.4 °F @温度73.4°F | ASTM D 4812 ASTM D 4812 | |
| Tensile Impact Strength 拉伸冲击强度 | 577 kJ/m² 577千焦耳/平方米 | 275 ft-lb/in² 275 ft-lb/in² | Type S; ASTM D 1822 S型，ASTM D 1822 | |
| Dart Drop, Total Energy 落锤，总能量 | 169 J 169 Ĵ @Temperature 23.0 °C @温度23.0°C | 125 ft-lb 125英尺-磅 @Temperature 73.4 °F @温度73.4°F | ASTM D 3029 ASTM D 3029 | |
| Impact Test 冲击试验 | 63.0 J 63.0 Ĵ @Temperature 23.0 °C @温度23.0°C | 46.5 ft-lb 46.5英尺-磅 @Temperature 73.4 °F @温度73.4°F | Instrumented Impact Total Energy; ASTM D 3763 仪器化冲击总能量，ASTM D 3763 | |
| Taber Abrasion, mg/1000 Cycles 泰伯磨耗，mg/1000周期 | 10.0 10.0 @Load 1.00 kg @费1.00公斤 | 10.0 10.0 @Load 2.20 lb @负载2.20磅 | CS-17; ASTM D 1044 CS-17，ASTM D 1044 | |
| Izod Impact, Notched 梁缺口冲击强度，缺口 | 8.01 J/cm 8.01焦耳/平方厘米 @Temperature 23.0 °C @温度23.0°C | 15.0 ft-lb/in 15.0 ft-lb/in @Temperature 73.4 °F @温度73.4°F | ASTM D 256 ASTM D 256 | |
| Electrical Properties 电气性能 | Metric 公 | English 英语 | Comments 评论 | |
| Volume Resistivity 体积电阻率 | >= 1.00e+17 ohm-cm > = 1.00E 17欧姆·厘米 | >= 1.00e+17 ohm-cm > = 1.00E 17欧姆·厘米 | ASTM D 257 ASTM D 257 | |
| Dielectric Constant 介电常数 | 2.96 2.96 @Frequency 1.00e+6 Hz @频率1.00E +6赫兹 | 2.96 2.96 @Frequency 1.00e+6 Hz @频率1.00E +6赫兹 | ASTM D 150 ASTM D 150 | |
| 3.17 3.17 @Frequency 50.0 - 60.0 Hz @频率50.0 - 60.0赫兹 | 3.17 3.17 @Frequency 50.0 - 60.0 Hz @频率50.0 - 60.0赫兹 | ASTM D 150 ASTM D 150 | ||
| Dielectric Strength 介电强度 | 14.9 kV/mm 14.9千伏/毫米 @Thickness 3.20 mm @厚度3.20毫米 | 378 kV/in 378千伏/ @Thickness 0.126 in @厚度0.126 | in air; ASTM D 149 在空气中，ASTM D 149 | |
| Dissipation Factor 耗散因数 | 0.000900 0.000900 @Frequency 50.0 - 60.0 Hz @频率50.0 - 60.0赫兹 | 0.000900 0.000900 @Frequency 50.0 - 60.0 Hz @频率50.0 - 60.0赫兹 | ASTM D 150 ASTM D 150 | |
| 0.0100 0.0100 @Frequency 1.00e+6 Hz @频率1.00E +6赫兹 | 0.0100 0.0100 @Frequency 1.00e+6 Hz @频率1.00E +6赫兹 | ASTM D 150 ASTM D 150 | ||
| Comparative Tracking Index 相比漏电起痕指数 | 250 - 400 V 250 - 400 V | 250 - 400 V 250 - 400 V | PLC code 2; UL 746A PLC代码，UL 746A | |
| Hot Wire Ignition, HWI 热丝引燃，HWI | 30.0 - 60.0 sec 30.0 - 60.0秒 | 30.0 - 60.0 sec 30.0 - 60.0秒 | PLC code 2; UL 746A PLC代码，UL 746A | |
| High Amp Arc Ignition, HAI 高安培电弧点火，海 | 60.0 - 120 arcs 60.0 - 120弧 | 60.0 - 120 arcs 60.0 - 120弧 | surface, PLC code 1; UL 746APLC代码1，UL 746A | |
| High Voltage Arc-Tracking Rate, HVTR 高压电弧跟踪率，HVTR | 25.4 - 80.0 mm/min 25.4 - 80.0毫米/分钟 | 1.00 - 3.15 in/min 1.00 - 3.15 /分钟 | PLC code 2; UL 746A PLC代码，UL 746A | |
| Thermal Properties 热性能 | Metric 公 | English 英语 | Comments 评论 | |
| CTE, linear, Parallel to Flow 热膨胀系数，线性，并行的流 | 68.4 µm/m-°C 68.4 μm/m-°C @Temperature -40.0 - 95.0 °C @温度-40.0 - 95.0°C | 38.0 µin/in-°F 38.0 μin/in-°F @Temperature -40.0 - 203 °F @温度-40.0 - 203°F | ASTM E 831 ASTM E 831 | |
| Specific Heat Capacity 比热容 | 1.25 J/g-°C 1.25 J/g-°C | 0.299 BTU/lb-°F 0.299 BTU/lb-°F | ASTM C 351 ASTM C 351 | |
| Thermal Conductivity 热传导率 | 0.270 W/mK 0.270 W / mK的 | 1.87 BTU-in/hr-ft²-°F 1.87 BTU-in/hr-ft² - °F | ASTM C 177 ASTM C 177 | |
| Deflection Temperature at 0.46 MPa (66 psi) 在0.46兆帕的热变形温度（66磅） | 137 °C 137 °C @Thickness 6.40 mm @厚度6.40毫米 | 279 °F 279 °F。 @Thickness 0.252 in @厚度0.252 | unannealed; ASTM D 8 未退火ASTM D 8 | |
| Deflection Temperature at 1.8 MPa (2 psi) 热变形温度在1.8兆帕（2磅） | 132 °C 132 °C @Thickness 6.40 mm @厚度6.40毫米 | 270 °F 270 °F。 @Thickness 0.252 in @厚度0.252 | unannealed; ASTM D 8 未退火ASTM D 8 | |
| Vicat Softening Point 维卡软化点 | 154 °C 154 °C | 309 °F 309 °F | Rate B/50; ASTM D 1525 B/50率，ASTM D 1525 | |
| UL RTI, Electrical UL RTI，电气 | 130 °C 130 °C | 266 °F 266 °F | UL 746B UL 746B | |
| UL RTI, Mechanical with Impact UL RTI，机械冲击 | 130 °C 130 °C | 266 °F 266 °F | UL 746B UL 746B | |
| UL RTI, Mechanical without Impact UL RTI，机械无冲击 | 130 °C 130 °C | 266 °F 266 °F | UL 746B UL 746B | |
| Flammability, UL94 易燃性，UL94 | HB HB @Thickness 0.710 mm @厚度0.710毫米 | HB HB @Thickness 0.0280 in @厚度0.0280 | UL 94 UL 94 | |
| Optical Properties 光学性质 | Metric 公 | English 英语 | Comments 评论 | |
| Refractive Index 折射率 | 1.586 1.586 | 1.586 1.586 | ASTM D 542 ASTM D 542 | |
| Haze 阴霾 | 1.00 % 1.00％ @Thickness 2.54 mm @厚度2.54毫米 | 1.00 % 1.00％ @Thickness 0.100 in @厚度0.100 | ASTM D 1003 ASTM D 1003 | |
| Transmission, Visible 传输，可见 | 88.0 % 88.0％ @Thickness 2.54 mm @厚度2.54毫米 | 88.0 % 88.0％ @Thickness 0.100 in @厚度0.100 | ASTM D 1003 ASTM D 1003 | |